Nitrile Disposable Glove

WRP NBR 3549

WRP NBR 3549 - E150
Main Features
  • Powder Free
  • Available in 240mm, 270mm and 290 mm lengths
  • Smooth and easy donning
  • Does not contain natural rubber latex
  • Soft comforatble formulation
  • Extra strong and durable
  • Protection against oils and alcohols
  • Suitable for food contact
symbol-01-(1).png

WRP NBR 3549 SPECIFICATION

Style No WRP NBR 3549 - E1 50
Surface Texture Finger tip
Process Single Chlorination
Weight per piece, g
(typical)
5.0g
Sizes XS - XXL
Palm Thickness
mm (min)
0.08
Length
(min)
240
Colours Blue
Main Applications
  • Medical
  • Laboratory
  • Chemo drugs handling
  • For Latex Allergic Users
  • Chemical handling
  • Janitorial & Sanitation
  • Agriculture
  • Food industry
  • Printing industry
  • Automotive industry
  • Electronics and electro plating industry
Product Conformance  
  • Medical Device: in compliance with European Medical Device Directive 93/42/EEC (CE Class I)
  • EN 455-1:2000, EN 455-2:2015, EN 455-3:2015, EN 455-4:2009
  • ASTM D6319
  • Personal Protective Equipment of Complex Design Category III, in compliance with 89/686/EEC, type tested to EN 420:2003+A1:2009, EN ISO 374-1:2016 Type B, EN 374-2:2014, EN 16523-1:2015, EN 374-4:2013 & EN ISO 374-5:2016, CE 2797
Quality Assurance  
  • US FDA Quality System Regulations (QSR)
  • ISO9001 Quality Mangement System
  • BS EN ISO13485 Quality Management Systems

  • Store in cool dry place
    Store in cool dry place
  • Single use only
    Single use only

Information on Ingredient

Chemical composition
  • NBR Synthetic Latex
  • Pottasium Hydroxide
  • Antioxidant
  • Rubber accelerator/Carbamates
  • Titanium dioxide
  • Sulphur
  • Zinc Oxide

Physical and Chemical Properties

Appearance Finger tip textured
Colour Blue

Palm Thickness

0.08 mm (min)
Glove Length 240 +/- 10 mm
Glove Weight 5.0g +/- 0.2 (For Size Medium)
Tensile strength at break 14 MPa min (unaged)
Elongation at break 500% min (unaged)
Tensile strength at break 14 MPa min (aged at 100C for 22 hours)
Elongation at break 400% min (aged at 100C for 22 hours)